PTFE Shrink Tubing transparency 22,23 / 6,20 mm, Box 2,5m

delivery time: 2 - 3 Tage nach unseren Betriebsferien ab 06.01.2025
Product.Nr.: 414619
weight: 0.170 kg
Manufacturer: Made in Germany

Business customers graduated prices after
registration in the login with your VAT ID.

36,57 EUR
(12,19 EUR pro Meter) incl. 19 % VATexcl. shipping costs

Discount

Quantity Single price Saving pro Meter
1-2 36,57 EUR 12,19 EUR
>= 3 34,01 EUR -7 % 11,34 EUR

PTFE Heat Shrink Tube 4:1  

Heat Shrink Tube PTFE transparent / clear 4:1 of modified crosslinked fluorpolymer, thin-walled, semi rigid  

PTFE heat shrink tubing made ​​of polytetrafluorethylen, color clear, shrink ratio 4:1, thin wall, semi rigid , highly flame retardant. Shrink tube PTFE is especialy designed for protecting applications in extreme electrical, chemical and thermal environments. Shrinking at + 350°C and is for permanent use at temperatures of -65°C to +260°C. Manufactured in Germany. 
PTFE heat shrinkable tube with internal diameters from 1.98mm to 50.8mm before shrinking by the meter in the blank according to your specifications, in practical mini-box (mini-box to 25,4mm before shrinkage) and as piece-goods

 

Specifications PTFE heat shrink tube 

Type PTFE
Color Transparency / clear
Material Polytetrafluorethylen
Material properties Thin-walled, semi rigid
Featuring Box
Inner Ø before shrinking 22,23 mm
Inner Ø after total shrinking 6.20 mm
Wall thickness after complete shrinkage  0.38 mm
Shrink Ratio 4:1
Continuous Operating Temperature -200°C bis +260°C
Shrink Temperature +350°C
Flammability Highly flame-retardant
Approvals / Specifications no approvals / chemically inert
Features RoHS Complient

 

Complete specifications PTFE heat shrink tubing as PDF for download

PTFE Heat Shrink Tube, quality tube Made in Germany

Downloads

50 Jahre MCE Mauritz Electronics

Ein halbes Jahrhundert technologische Exzellenz Mehr »